Hot metal detector thermal analysis sample cup for casting iron analysis

Views : 289
Update time : 2016-11-15 08:28:54

Hot metal detector thermal analysis sample cup for casting iron analysis

Carbon Cup (also known as thermal analysis sample cup, pour sample cup) it is well-designed sample cup, high-precision thermocouples. Thermal analysis because of its fast, simple, reliable and low cost is widely used in the field of hot metal composition control, when the molten iron is poured into the sample cup, gradually solidified molten iron over time, according to the thermal analysis of the cooling curve of the temperature of the platen, measured and calculated the CEL, C, Si and other ingredients 
Principle:
Liquid iron blast furnace analyzer is my company after years of research to improve the measurement accuracy of the use of higher and more stable management of the latest generation of blast furnace hot metal instrument. Iron Front rapid thermal analysis technique based on the solidification temperature curve Cast Iron formation of the measured object, the solidification temperature curve mathematical analysis, the different components of the characteristic curve point.
 Iron calculated carbon equivalent (CE) carbon content (C%) based on mathematical equations, previously identified, a silicon content of cast iron blast furnace (Si%) and other indicators of rapid analysis techniques, the measurement accuracy can be achieved CE 0.10, C 0.05%, Si 0.10% is a simple cast iron production in blast furnace use, fast, accurate instrument. 
 Thermal analyzer were pouring time is about two minutes to complete the detection of hot metal in the waiting time, and then automatically calculate the carbon agent, ferrosilicon, put the amount of scrap iron component is adjusted to obtain a suitable hot metal composition after .
Chinese instrument uses 220 v
Main features:
1.The detection of carbon, silicon,
2. The detection of carbon equivalent
3. The rate of the ball, creep rate determination
4. Tensile strength determination
5. Setting the target material
6. Put the amount is automatically calculated by the amount of carbon agent, ferrosilicon, steel scrap
7. Automatic drawing carbon-silicon, carbon equivalent, primary crystallization temperature eutectic temperature graph, then the printer can print
8. Preservation and reproduction of data
9. Then the printer can print data, copy the picture
10. Celsius / Fahrenheit switching
11. The primary crystallization temperature, measured eutectic temperature

12. Equipped with 20 calibration curve can be set according to each plant molten iron real standard case, the more accurate detection.